Inhibiting corrosion and hydrogen embrittlement in carbon steel during pickling
Publication details: mayo 2009Description: 7 p. ; 46-52 In: Materials Performance 48Summary: Transcripción del resumen del autor. Steel must be protected from corrosion and hydrogen embrittlement (HE) during pickling. This work examined the corrosion and HE behavior of carbon steel in 1 M hydrochloric acid (HCl). Three organic inhibitors were used for potentiodynamic testing and cathodic charging. A correlation between corrosion and HE inhibition was established.| Current library | Status | Barcode | |
|---|---|---|---|
| Biblioteca Alejandro Angel Bulgheroni | Not for loan | 200047783 |
Transcripción del resumen del autor. Steel must be protected from corrosion and hydrogen embrittlement (HE) during pickling. This work examined the corrosion and HE behavior of carbon steel in 1 M hydrochloric acid (HCl). Three organic inhibitors were used for potentiodynamic testing and cathodic charging. A correlation between corrosion and HE inhibition was established.