Inhibiting corrosion and hydrogen embrittlement in carbon steel during pickling
Abdel-Karim, R. El-Raghy, S. Waheed, A.F.
Inhibiting corrosion and hydrogen embrittlement in carbon steel during pickling - mayo 2009 - 7 p. ; 46-52
Transcripción del resumen del autor. Steel must be protected from corrosion and hydrogen embrittlement (HE) during pickling. This work examined the corrosion and HE behavior of carbon steel in 1 M hydrochloric acid (HCl). Three organic inhibitors were used for potentiodynamic testing and cathodic charging. A correlation between corrosion and HE inhibition was established.
5
Inhibiting corrosion and hydrogen embrittlement in carbon steel during pickling - mayo 2009 - 7 p. ; 46-52
Transcripción del resumen del autor. Steel must be protected from corrosion and hydrogen embrittlement (HE) during pickling. This work examined the corrosion and HE behavior of carbon steel in 1 M hydrochloric acid (HCl). Three organic inhibitors were used for potentiodynamic testing and cathodic charging. A correlation between corrosion and HE inhibition was established.
5