Erosion-corrosion failure of a spiral heat exchanger
Publication details: dic. 2007Description: 3 p. ; 50-52 In: Materials Performance 46Summary: This article discusses a failure on a type 316 stainless steel (UNS316000) spiral heat exchanger. The failure occurred just five months after the equipmet had been put into service. The study showed that degradation occurred from erosion-corrosion in the vicinity of the spacers between the metal sheets| Current library | Status | Barcode | |
|---|---|---|---|
| Biblioteca Alejandro Angel Bulgheroni | Not for loan | 200042068 |
This article discusses a failure on a type 316 stainless steel (UNS316000) spiral heat exchanger. The failure occurred just five months after the equipmet had been put into service. The study showed that degradation occurred from erosion-corrosion in the vicinity of the spacers between the metal sheets