Erosion-corrosion failure of a spiral heat exchanger
Erosion-corrosion failure of a spiral heat exchanger
- dic. 2007
- 3 p. ; 50-52
This article discusses a failure on a type 316 stainless steel (UNS316000) spiral heat exchanger. The failure occurred just five months after the equipmet had been put into service. The study showed that degradation occurred from erosion-corrosion in the vicinity of the spacers between the metal sheets
12
This article discusses a failure on a type 316 stainless steel (UNS316000) spiral heat exchanger. The failure occurred just five months after the equipmet had been put into service. The study showed that degradation occurred from erosion-corrosion in the vicinity of the spacers between the metal sheets