| 245 | 0 | 0 | _aStress cracking of stainless steel safety gate valve stem |
| 260 |
_a _b _cfeb. 2008 |
||
| 270 | _a01/08/2011 ; 01/08/2011 | ||
| 300 | _a4 p. ; 64-67 | ||
| 520 | _aTranscripción del resumen del autor. This study investigated the failure of a 15-5 PH (UNS S15500) precipitation-hardened stainless steel stem when installed in a 5 1/8in. (130-mm) hydraulic surface safety gate valve working in a sour gas environment. The results indicate that the fracture failure was caused by sulfide stress cracking, which progressed transgranularly in the martensitic matrix. | ||