Microstructural analysis of ethylene furnace steel alloy tubes
Publication details: mayo 2011Description: 7 p. ; 58-64 In: Materials Performance 50Summary: Transcripción del resumen del autor. Several radiant tubes of n ethylene (C2H4) furnace at a petrochemical plant were analyzed after failure. Experimental results suggest that the failures were caused by exposure of the tubes to excessive temperature during service. It was recommended that the furnace temperature be closely controlled to avoid averheating the tubes| Current library | Status | Barcode | |
|---|---|---|---|
| Biblioteca Alejandro Angel Bulgheroni | Not for loan | 200053859 |
Transcripción del resumen del autor. Several radiant tubes of n ethylene (C2H4) furnace at a petrochemical plant were analyzed after failure. Experimental results suggest that the failures were caused by exposure of the tubes to excessive temperature during service. It was recommended that the furnace temperature be closely controlled to avoid averheating the tubes