01459nab a2200205 4500 20260520002032.0 260224s2011 xxu Corrosion of E-glass fiber in simulated oilfield environments agos. 2011 04/04/2012 ; 04/04/2012 5 p. ; 371 - 375 Transcripción del resumen del autor. In order to have a better understanding of corrosion behaviors and mechanisms of E-glass fibers in oilfield environments, three different oilfield atmospheres including CO2, H2S and Cl- were firstly given. After different simulated corrosion tests, morphologies of E-glass fibers were gathered using SEM. Chemical bonding status and elemental analysis were systematically investigated by XPS, FT-IR and EDS. The results revealed that corrosion of E-glass fibers in simulated oilfield acidic media was primarily attributed to ion exchange mechanism, which was not only controlled by acid concentration, but also dominated by formation of complex ions or insoluble salts. The depletion of cations on E-glass fiber surface can disrupt the continuity of glass network, thus disturb the glass structure, therefore reducing the strength of fibers. 2 Journal of Petroleum Science & Engineering 78 ARTICULO Li, Houbu 52353 Yan, Milin 52354 Qi, Dongtao 52355 187000 187000 0 0 0 0 254819 BAAB BAAB 2026-03-06 200059104 0 200059104 2026-03-06 00:16:00 2026-03-06 ARTICULO