TI  - Stress cracking of stainless steel safety gate valve stem
PY  - 2008///
CY  - 
PB  - 
N2  - Transcripción del resumen del autor. This study investigated the failure of a 15-5 PH (UNS S15500) precipitation-hardened stainless steel stem when installed in a 5 1/8in. (130-mm) hydraulic surface safety gate valve working in a sour gas environment. The results indicate that the fracture failure was caused by sulfide stress cracking, which progressed transgranularly in the martensitic matrix