01995nab a2200205 4500 20260520000949.0 260224s2010 xxu Characterizing the relaxation of the open-circuit potential during an AC-DC-AC accelerated test sep. 2010 13/09/2010 ; 13/09/2010 11 p. ; 095001 Transcripción del resumen del autor. The non-conventional accelerated alternating current-direct current-alternating current (AC-DC-AC) testing method for organic coatings induces degradation by promoting cathodic reactions at the metal coating interface and ionic transport in the bulk of the coating. This cyclic method involves a testing step in which the coating properties are determined using electrochemical impedance spectroscopy (EIS), a DC step in which a cathodic potential is applied for a given time period, and a relaxation step where the coating is allowed to relax back to a stable open-circuit potential (EOC) condition. Analysis of the relaxation EOC profile has been reported where characteristic times were attributed to the transport of ions through the coating, dielectric relaxation of the coating, and charge transfer at the metal/coating interface. The AC-DC-AC degradation of a standard United States Army vehicle epoxy primer on a steel substrate is reported here. The influences of applied DC potential and temperature were determined by subjecting the coating to potentials of -2 V and -8 V relative to the stable EOC at temperatures ranging from 25°C to 65°C. The relaxation EOC profiles were analyzed with a mathematical model to yield the characteristic times associated with the processes involved and the consistency of these processes with Arrhenius behavior was determined. 9 Corrosion 66 ARTICULO Allahar, K.N. 40322 Upadhyay, V. 46835 Bierwagen, G.P. 43352 176894 176894 0 0 0 0 244713 BAAB BAAB 2026-03-05 200048829 0 200048829 2026-03-05 18:57:48 2026-03-05 ARTICULO