00994nab a2200205 4500 20260520002923.0 260224s2010 xxu Sulfide stress cracking of a S135 drill pipe mar. 2010 18/08/2010 ; 18/08/2010 4 p. ; 66-69 Transcripción del resumen del autor. This work investigated and analyzed a length of S135 drill pipe that broke durircg pumping from a well that contained hydrogen sulfide (H2S). There was no obvious plastic deformation at the drill pipe fracture. The pipe material met API Specification 5D, but was sensitive to sulfide stress cracking (SSC). The fracture morphology revealed typical H2S stress corrosion cracking and the failure was attributed to SSC. 3 Materials Performance 49 ARTICULO Lv, Shuan-lu 46472 Yuan, Peng-Bin 46330 Luo, Fa-qian 46473 176110 176110 0 0 0 0 243929 BAAB BAAB 2026-03-05 200048029 0 200048029 2026-03-05 18:56:46 2026-03-05 ARTICULO