01382nab a2200193 4500 20260520000938.0 260224s2010 xxu Corrosion behavior of Cr-Mn-Ni stainless steel in acetic acid solution ago. 2010 10/08/2010 ; 10/08/2010 9 p. ; 085004 Transcripción del resumen del autor. Corrosion behavior of a Cr-Mn-Ni stainless steel designated as J204 (DIN 1.4376) was evaluated in acetic acid (CH3COOH) solutions by electrochemical methods and boiling immersion tests. Resistance to stress corrosion cracking (SCC) was evaluated using U-bend and slow strain rate tests (SSRT). The influence of acid concentrations, temperature, and chloride ions on the corrosion resistance of the alloy was investigated. J204 stainless steel was found comparable with AISI 304 (UNS S30400) stainless steel in a wide range ofCH3COOH solutions. The chemistry of the passive film formed in 98% (glacial) CH3COOH environment was evaluated using x-ray photoelectron spectroscopy (XPS). This analysis revealed enrichment of Cr ions on the surface in the form of chromium oxide, irrespective of Ni content in the stainless steel. 8 Corrosion 66 ARTICULO Shankar Rao, V. 46337 Singhal, L.K. 46338 175896 175896 0 0 0 0 243715 BAAB BAAB 2026-03-05 200047807 0 200047807 2026-03-05 18:56:29 2026-03-05 ARTICULO