01799nab a2200205 4500 20260520000856.0 260224s2009 xxu Corrosion Behavior of Mg-Al Alloys with Aluminum Thermal Spray Coatings in Humid and Saline Environments dic. 2009 07/07/2010 ; 06/07/2010 14 p. ; 817-830 Transcripción del resumen del autor. The corrosion behavior of thermal spray aluminum coatings deposited on AZ31 (UNS M11311), AZ80 (UNS M11800), and AZ91D (UNS M11916)Mg-Al alloys was evaluated in salt water (3.5 wt% sodium chloride [NaCl]), neutral salt fog (ASTM B117), and high relative humidity (98% RH, 50°C) environments. The changes in the morphology and corrosion behavior of the aluminum coatings induced by cold-pressing posttreatment were also examined. In chloride-containing environments, the presence of interconnected pores in the as-sprayed aluminum coatings facilitated the galvanic acceleration of the corrosion of the magnesium substrates. The cold-pressed aluminum coatings revealed improved corrosion behavior associated with a lower level of porosity. In high-humidity environments, even though the corrosion rates for all the examined materials were lower than in the case of salt fog, similar corrosion features were observed; formation of hydromagnesite on the surface of untreated materials, galvanic corrosion in the Al-TS specimens, and almost negligible corrosion attack of the aluminum coating with formation of bayerite (ß-Al2O3·3H2O) in the case of the cold-pressed specimens. 12 Corrosion 65 ARTICULO Arrabal, R. 43511 Pardo, A. 34232 Merino, M.C. 34233 171806 171806 0 0 0 0 239625 BAAB BAAB 2026-03-05 200046679 0 200046679 2026-03-05 15:14:11 2026-03-05 ARTICULO