Reasons for Crack Arrest in Stress Corrosion Cracking tests-crack propagation rate in high-strength steels (Record no. 175698)
[ view plain ]
| 000 -LEADER | |
|---|---|
| fixed length control field | 01548nab a2200205 4500 |
| 008 - CÓDIGOS DE INFORMACIÓN DE LONGITUD FIJA - INFORMACIÓN GENERAL | |
| Campo de control de longitud fija | 260224s2009 xxu |
| 100 1# - RESPONSABLE PERSONAL | |
| Apellido, Nombre | Sanchez, J. |
| 9 (RLIN) | 40325 |
| 100 1# - RESPONSABLE PERSONAL | |
| Apellido, Nombre | Andrade, C. |
| 9 (RLIN) | 40326 |
| 100 1# - RESPONSABLE PERSONAL | |
| Apellido, Nombre | Fullea, J. |
| 9 (RLIN) | 46186 |
| 245 00 - TITULO | |
| Título | Reasons for Crack Arrest in Stress Corrosion Cracking tests-crack propagation rate in high-strength steels |
| 260 ## - PUBLICACION, DISTRIBUCION, ETC | |
| Lugar de publicación, distribución, etc. | |
| Nombre de publicador, distribuidor, etc. | |
| Fecha de publicación, distribución, etc. | jun. 2009 |
| 270 ## - FECHA DE CARGA | |
| Fecha de carga | 03/08/2010 ; 03/08/2010 |
| 300 ## - DESCRIPCION FISICA | |
| Otra extensión | 8 p. ; 368-375 |
| 520 ## - RESUMEN, ETC | |
| Resumen | Transcripción del resumen del autor. The stress corrosion cracking (SCC) process that occurs in metals is at present not a fully elucidated mechanism of deterioration. It is a surface process that implies a corrosion and stress synergy, but the most practical consequence is that SCC can modify the mechanical characteristics of the metal, causing brittle failure. The process generally involves a high level of uncertainty in the prediction. This research deals with steels used in prestressed concrete and is designed to determine why, in the early stages of the crack, this can stop or continue. That is, some cracks initiate and do not continue to grow, while others advance and cause failure. The electrochemical response has been studied as cracks initiate and grow, and the effects of mechanical parameters on crack propagation were evaluated. Crack growth was determined by measuring crack opening displacement and using the flexibility method to obtain crack depth. |
| 581 ## - ESTADO DE COLECCIÓN | |
| Estado de colección | 6 |
| 773 ## - CORRECCIÓN | |
| Partes relacionadas | |
| 942 ## - DESC. DE MATERIAL | |
| Tipo de item KOHA | Artículo de Revista |
| Biblioteca propietaria | Biblioteca actual | Fecha de adquisición | Inventario | Total de préstamos | Inventario | Fecha de carga | Tipo de item KOHA |
|---|---|---|---|---|---|---|---|
| Biblioteca Alejandro Angel Bulgheroni | Biblioteca Alejandro Angel Bulgheroni | 05/03/2026 | 200047600 | 200047600 | 05/03/2026 | Artículo de Revista |