Stress cracking of stainless steel safety gate valve stem
Mostofi, J. Zamanian, M.
Stress cracking of stainless steel safety gate valve stem - feb. 2008 - 4 p. ; 64-67
Transcripción del resumen del autor. This study investigated the failure of a 15-5 PH (UNS S15500) precipitation-hardened stainless steel stem when installed in a 5 1/8in. (130-mm) hydraulic surface safety gate valve working in a sour gas environment. The results indicate that the fracture failure was caused by sulfide stress cracking, which progressed transgranularly in the martensitic matrix.
2
Stress cracking of stainless steel safety gate valve stem - feb. 2008 - 4 p. ; 64-67
Transcripción del resumen del autor. This study investigated the failure of a 15-5 PH (UNS S15500) precipitation-hardened stainless steel stem when installed in a 5 1/8in. (130-mm) hydraulic surface safety gate valve working in a sour gas environment. The results indicate that the fracture failure was caused by sulfide stress cracking, which progressed transgranularly in the martensitic matrix.