Comparative Study on The Photocatalytic Hydrogen Production from Methanol over Cu-, Pd-, Co- and Au-Loaded TiO2
Language: Inglés Publication details: sept./oct. 2015Description: 8 p. ; 831-839 In: Oil and Gas Science and Technology 70Summary: Transcripción del resumen del autor: Photocatalytic hydrogen production from a methanol-water solution was investigated in a semi-continuous reactor over different metal-loaded TiO2 catalysts under UltraViolet (UV) light irradiation. The catalysts were mainly prepared by the incipient wetness impregnation method by varying the metal weight ratio in the range of 1-10 wt%. The effects of metal loading and H2 pre-treatment on the photocatalytic activity were investigated. In addition, the activity of the catalysts was also compared with a reference Au-TiO2 catalyst from the World Gold Council (WGC). The photocatalysts were characterized by using X-Ray Diffraction (XRD) and N2 physisorption before and after the activity measurements. The photocatalytic activity decreased in the order of Pd > Au > Cu > Co in the comparative study of Cu-TiO2, Co-TiO2, Au-TiO2 and Pd-TiO2. Optimum hydrogen evolution was achieved with 5 wt% Pd-TiO2 and 5 wt% Cu-TiO2.| Current library | Status | Barcode | |
|---|---|---|---|
| Biblioteca Alejandro Angel Bulgheroni | Not for loan | 200061662 |
Transcripción del resumen del autor: Photocatalytic hydrogen production from a methanol-water solution was investigated in a semi-continuous reactor over different metal-loaded TiO2 catalysts under UltraViolet (UV) light irradiation. The catalysts were mainly prepared by the incipient wetness impregnation method by varying the metal weight ratio in the range of 1-10 wt%. The effects of metal loading and H2 pre-treatment on the photocatalytic activity were investigated. In addition, the activity of the catalysts was also compared with a reference Au-TiO2 catalyst from the World Gold Council (WGC). The photocatalysts were characterized by using X-Ray Diffraction (XRD) and N2 physisorption before and after the activity measurements. The photocatalytic activity decreased in the order of Pd > Au > Cu > Co in the comparative study of Cu-TiO2, Co-TiO2, Au-TiO2 and Pd-TiO2. Optimum hydrogen evolution was achieved with 5 wt% Pd-TiO2 and 5 wt% Cu-TiO2.
5